Sem/edx laboratories in the USA right now? Analysis and Results: The submitted bottle was examined for signs of interior distress, and the water from the bottle was removed and maintained. Some of the suspended particulate was filtered and examined non-destructively by light microscopy first, to characterize the material. A low magnification stereo microscope image of the filtered white particulate is shown in the image above. From this image, biological tissues were ruled out, and the material was observed to be crystalline. Polarized light microscopy (PLM) was used to analyze the sample next. From this examination, the material showed birefringence as shown in the PLM image on the right. The PLM Image Stereo Microscope image suspect material showed optical properties and morphology dissimilar to common carbonates and sulfates. It was determined to be a birefringent crystalline material, but it could not be identified using only PLM methods. Therefore, analysis using scanning electron microscopy with energy dispersive x-ray spectroscopy (SEM-EDS) would have to be performed to obtain further information about the suspect material.
Translucent or transparent coatings on metallic or semi-conductor substrates are very difficult to image due to their reflective nature. Nomarski/DIC imaging is an effective method for accentuating differences in thickness, density or the optical index in these cases. This analysis enhances and highlights subtle features with brilliant color gradients and captures them with a high resolution digital imaging system. Let us bring out your sample’s hidden features.
How do I submit a sample or a set of samples? To submit a sample or set of samples, please see the page How to Submit Samples. What if I believe my samples are hazardous? We are not equipped to handle or dispose of every kind of hazardous material. Please call us before sending in any potentially hazardous samples. In cases where we are able to analyze your harzardous samples we may not be able to dispose of them and therefore we will return them to you. See extra details at microvisionlabs.com. ?We partner with companies in all phases of product development and sales, including R&D, manufacturing, QC, advertising and failure analysis. Our laboratory offers a highly-trained and experienced staff utilizing a powerful set of analytical tools (SEM with EDS and backscatter detectors, Bruker X-Flash elemental mapping, X-Ray imaging, Micro-FTIR spectroscopy, Micro-XRF, light microscopy, cross sectioning/precision polishing and microhardness testing).
Close examination of any possible defects or voids was undertaken at higher magnification. The voids did not appear to create any structural or conductivity issues. Additionally, the formation and contiguity of intermetallic bonds between the contacts and solder were shown using a combination of EDS line scan elemental spectroscopy and elemental mapping. The SEM image and the EDS map to the left show the intermetallic layer between the copper wire and the tin/lead solder via the mixture of the red copper and the blue tin.
A client responsible for maintaining the facilities in a public school district called with concerns of a possible mold problem. Areas with high foot traffic, especially those where students tracked water in, were showing dark black spots in the floor tiles. Aggressive cleaning and buffing of the floor would remove the problem for a while, but after several few weeks, the problem resurfaced. The facilities management staff was convinced it was mold related, but sending samples, swabs, and air grabs to a mold lab for culturing showed no sign of fungal structures on the tiles. Read extra info on this website.